30% Glass Fiber Reinforced Nylon 6 Material (PA6 GF30)

30% Glass Fiber Reinforced Nylon 6 Material (PA6 GF30)
классификация: Glass Fiber Reinforced Nylon
ALL AROUND POLYMER CO., LTD.
ALL AROUND POLYMER CO., LTD.
Страна: Taiwan
Телефон: +886-6-5998877
Контактное лицо: WU YAN-SHEN
Запрос сейчас

PA6 30% Glass Fiber Reinforced (PA6 GF30), also known as PA6 GF30 material or 30 glass filled nylon, is a widely used engineering plastic with excellent mechanical strength, rigidity, and heat resistance. This nylon compound performs consistently across different environments, offering easy injection molding, a smooth surface finish, and robust structural support.

  • Material: Nylon 6 (PA6/ Polyamide 6)

  • Glass Fiber Content: 30%

  • Tensile Strength: 165 MPa

  • Elongation at Break: 3%

  • Notched Impact Strength (23°C): 12 kJ/m²

  • Density: 1.38 g/cm³

  • Melting Point: 230°C

  • Color: Natural, Black, and other custom colors available

With its durable properties, PA6 GF30 material is ideal for various industrial applications:

  • Automotive Industry: This PA6 glass fiber reinforced material is commonly used in automotive parts like interior components, car key casings, and mirror housings. The 30% glass fiber provides enhanced mechanical properties, making it suitable for parts requiring strength, rigidity, and stability in standard automotive environments.

  • Electronics and Appliances: This nylon compound is well-suited for electronic and appliance components, such as plugs, outdoor faucet bases, and appliance housings. Its heat resistance and insulation properties make PA6 GF30 material an ideal choice for high-temperature environments.

  • Office Furniture: PA6 GF30 is also widely applied in office furniture components, including chair adjusters and drawer slides. Its 30 glass filled nylon formulation offers both strength and cost-efficiency, ensuring long-term performance in high-use applications.

Technical Specification Comparison of PA6 GF30 and Other PA6 GF meterials
 

PA6 GF30

PA6 GF15

PA6 GF40

PA6 GF50

PA6 GF60
Tensile Strength 165Mpa 118MPa 185Mpa 200Mpa 220Mpa
Elongation at Break 3% 3.3% 2.8% 2% 2%
Impact Strength (Notched) 12 kJ/m² 10 kJ/m² 13 kJ/m² 14 kJ/m² 14 kJ/m²
Density 1.38 g/cm³ 1.21 g/cm³ 1.46 g/cm³ 1.56 g/cm³ 1.67 g/cm³
Properties Test Method    Units Conditions Value
Density ISO 1183 g/cm3 Dry 1.38
Tensile strength at break ISO 527
(50mm/min)		 Mpa Dry
Cond.		 165
130
Elongation at break ISO 527
(50mm/min)		 % Dry
Cond.		 3
4.5
Impact strength ISO 180-1C
Charpy,23℃		 Kj/㎡ Dry
Cond.		 75
80
Impact strength ISO 180-1C
Charpy,-30℃		 Kj/㎡ Dry
Cond.		 72
78
Notched impact strength ISO 180-1A
Charpy,23℃		 Kj/㎡ Dry
Cond.		 12
15
Notched impact strength ISO 180-1A
Charpy,-30℃  		 Kj/㎡ Dry
Cond.		 11
11
Melting point ISO 3146C DSC ℃ Dry 230